收藏词条 编辑词条 日本承压铸钢
表5-94 高温高压用铸钢的钢号和化学成分(质量分数)(%)
钢 号 |
C |
Si |
Mn |
P ≤ |
S ≤ |
Cr |
Mo |
其他 |
SCPH1 |
≤0.25 |
≤0.60 |
≤0.70 |
0.040 |
0.040 |
— |
— |
— |
SCPH2 |
≤0.30 |
≤0.60 |
≤1.00 |
0.040 |
0.040 |
— |
— |
— |
SCPH11 |
≤0.25 |
≤0.60 |
0.50~0.80 |
0.040 |
0.040 |
— |
0.45~0.65 |
— |
SCPH21 |
≤0.20 |
≤0.60 |
0.50~0.80 |
0.040 |
0.040 |
1.00~1.50 |
0.45~0.65 |
— |
SCPH22 |
≤0.25 |
≤0.60 |
0.50~0.80 |
0.040 |
0.040 |
1.00~1.50 |
0.90~1.20 |
— |
SCPH23 |
≤0.20 |
≤0.60 |
0.50~0.80 |
0.040 |
0.040 |
1.00~1.50 |
0.90~1.20 |
V 0.15~0.25 |
SCPH32 |
≤0.20 |
≤0.60 |
0.50~0.80 |
0.040 |
0.040 |
2.00~2.75 |
0.90~1.20 |
— |
SCPH61 |
≤0.20 |
≤0.75 |
0.50~0.80 |
0.040 |
0.040 |
4.00~6.50 |
0.45~0.65 |
— |
b.高温高压用铸钢的残余元素含量,见表5-94。
表5-94 高温高压用铸钢的残余元素含量(质量分数)(%)
钢 号 |
Cu |
Ni |
Cr |
Mo |
W |
残余元素总量 |
SCPH1 |
0.50 |
0.50 |
0.25 |
0.25 |
— |
1.00 |
SCPH2 |
0.50 |
0.50 |
0.25 |
0.25 |
— |
1.00 |
SCPH11 |
0.50 |
0.50 |
— |
— |
0.10 |
1.00 |
SCPH21 |
0.50 |
0.50 |
— |
— |
0.10 |
1.00 |
SCPH22 |
0.50 |
0.50 |
— |
— |
0.10 |
1.00 |
SCPH23 |
0.50 |
0.50 |
— |
— |
0.10 |
1.00 |
SCPH32 |
0.50 |
0.50 |
— |
— |
0.10 |
1.00 |
SCPH61 |
0.50 |
0.50 |
— |
— |
0.10 |
1.00 |
c.高温高压用铸钢的的力学性能,见表5-96。
表5-96 高温高压用铸钢的的力学性能
钢 号 |
力学性能(不小于) |
|||
σb /MPa |
σs / Mpa |
δ (%) |
ψ (%) |
|
SCPH1 |
410 |
205 |
21 |
35 |
SCPH2 |
480 |
245 |
196 |
35 |
SCPH11 |
450 |
245 |
22 |
35 |
SCPH21 |
480 |
275 |
17 |
35 |
SCPH22 |
550 |
345 |
16 |
35 |
SCPH23 |
550 |
345 |
13 |
35 |
SCPH32 |
480 |
275 |
17 |
35 |
SCPH61 |
620 |
410 |
17 |
35 |
(2) 日本JIS标准低温高压用铸钢[JIS G5152(1991)]
a.低温高压用铸钢的钢号与化学成分,见表5-97。
表5-97 低温高压用铸钢的钢号和化学成分(质量分数)(%)
钢 号 |
C |
Si |
Mn |
P ≤ |
S ≤ |
Cr |
Ni |
Mo |
其他 |
残余元素总量 |
SCPL1 |
≤0.30 |
≤0.60 |
≤1.00 |
0.040 |
0.040 |
≤0.25 |
≤0.50 |
— |
Cu≤0.50 |
≤1.00 |
SCPL11 |
≤0.25 |
≤0.60 |
0.50~0.80 |
0.040 |
0.040 |
≤0.35 |
— |
0.45~0.65 |
Cu≤0.50 |
≤1.00 |
SCPL21 |
≤0.25 |
≤0.60 |
0.50~0.80 |
0.040 |
0.040 |
≤0.035 |
2.00~3.00 |
— |
Cu≤0.50 |
≤1.00 |
SCPL31 |
≤0.15 |
≤0.60 |
0.50~0.80 |
0.040 |
0.040 |
≤0.35 |
3.00~4.00 |
— |
Cu≤0.50 |
≤1.00 |
b.低温高压用铸钢的力学性能,见表5-98。
表5-98 低温高压用铸钢的力学性能
钢 号 |
力学性能(不小于) |
冲击吸收功(V型缺口) |
|||||
σb /MPa |
σs / Mpa |
δ (%) |
ψ (%) |
实验温度 /oC |
平均值 ≥/J |
单个值 ≥/J |
|
SCPL1 |
450 |
245 |
21 |
35 |
-45 |
18 |
14 |
SCPL11 |
450 |
245 |
21 |
35 |
-60 |
18 |
14 |
SCPL21 |
480 |
275 |
21 |
35 |
-75 |
21 |
17 |
SCPL31 |
480 |
275 |
21 |
35 |
-100 |
21 |
17 |