收藏词条 编辑词条 预应力钢丝及钢绞线用热轧盘条(YB/T146-1998)
(2)尺寸规格盘条的尺寸规格及允许偏差应在合同中注明，未注明者,应符合GB/T14981中B级的规定。
(3)牌号和化学成分见表1。
表1 预应力钢丝及钢绞线用热轧盘条的牌号和化学成分
|
牌 号 |
化学成分(质量分数)(%) |
|||||
|
C |
Si |
Mn |
P |
S |
Cu |
|
|
|
0.70～0.75 |
0.12～0.32 |
0.30～0.60 |
≤0.025 |
≤0.025 |
≤0.20 |
|
72MnA |
0.70～0.75 |
0.12～0.32 |
0.60～0.90 |
≤0.025 |
≤0.025 |
≤0.20 |
|
|
0.73～0.78 |
0.12～0.32 |
0.30～0.60 |
≤0.025 |
≤0.025 |
≤0.20 |
|
75MnA |
0.73～0.78 |
0.12～0.32 |
0.60～0.90 |
≤0.025 |
≤0.025 |
≤0.20 |
|
|
0.75～0.80 |
0.12～0.32 |
0.30～0.60 |
≤0.025 |
≤0.025 |
≤0.20 |
|
77MnA |
0.75～0.80 |
0.12～0.32 |
0.60～0.90 |
≤0.025 |
≤0.025 |
≤0.20 |
|
|
0.78～0.83 |
0.12～0.32 |
0.30～0.60 |
≤0.025 |
≤0.025 |
≤0.20 |
|
80MnA |
0.78～0.83 |
0.12～0.32 |
0.60～0.90 |
≤0.025 |
≤0.025 |
≤0.20 |
|
|
0.80～0.85 |
0.12～0.32 |
0.30～0.60 |
≤0.025 |
≤0.025 |
≤0.20 |
|
82MnA |
0.80～0.85 |
0.12～0.32 |
0.60～0.90 |
≤0.025 |
≤0.025 |
≤0.20 |
(4)力学性能见表2。
|
牌 号 |
力学性能 |
|||
|
抗拉强度 ób/MPa |
断面收缩率妒ψ(%) |
抗拉强度ób/MPa |
断面收缩率ψ(%) |
|
|
直径8.0～10 |
直径10.5～13 |
|||
|
|
960～1080 |
≥25% |
940～1060 |
≥25% |
|
72MnA |
990～1110 |
970～1090 |
||
|
75MnA |
1020～1140 |
1000～1120 |
||
|
77MnA |
1040～1160 |
1020～1140 |
||
|
80MnA |
1060～1180 |
1040～1160 |
||
|
82MnA |
1080～1200 |
1060～l180 |
||