收藏词条 编辑词条 JIS G 4312-1991耐热钢板
形状、尺寸、重量及其允许偏差
标准尺寸,见表1。
表1 标准尺寸
厚度 |
宽度×长度 |
|
3.0 4.0 5.0 6.0 7.0 8.0 9.0 10.0 |
12.0 15.0 20.0 25.0 30.0 35.0 |
1000×2000 1219×2438 1219×3048 1500×3000 1521×3048 |
热轧钢板的厚度允许偏差,见表2和表3。而表3只有当需方指明要求时才适用。
表2 热轧钢板厚度允许偏差(mm)
厚度 |
宽度 |
||||||
<1000 |
1000~ <1250 |
1250~ <1600 |
1600~ <2000 |
2000~ <2500 |
2500~ <3150 |
3150~ <4000 |
|
2.50~<3.15 |
±0.25 |
±0.30 |
±0.35 |
— |
— |
— |
— |
3.15~<4.00 |
±0.30 |
±0.35 |
±0.40 |
— |
— |
— |
— |
4.00~<5.00 |
±0.38 |
±0.40 |
±0.45 |
±0.60 |
±0.80 |
±1.0 |
— |
5.00~<6.00 |
±0.45 |
±0.45 |
±0.50 |
±0.70 |
±0.90 |
±1.1 |
— |
6.00~<8.00 |
±0.55 |
±0.60 |
±0.60 |
±0.75 |
±1.0 |
±1.2 |
±1.4 |
8.00~<10.0 |
±0.65 |
±0.65 |
±0.65 |
±0.80 |
±1.2 |
±1.5 |
±1.6 |
10.0~<16.0 |
±0.70 |
±0.70 |
±0.70 |
±0.85 |
±1.2 |
±1.5 |
±1.6 |
16.0~<25.0 |
±0.80 |
±0.80 |
±0.80 |
±0.95 |
±1.3 |
±1.5 |
±1.6 |
25.0~<40.0 |
±0.90 |
±0.90 |
±0.90 |
±1.1 |
±1.3 |
±1.5 |
±1.6 |
40.0~<63.0 |
±1.0 |
±1.0 |
±1.2 |
±1.2 |
±1.4 |
±1.5 |
±1.6 |
63.0~<100 |
±1.1 |
±1.2 |
±1.3 |
±1.3 |
±1.5 |
±1.6 |
±1.7 |
100~<160 |
±1.3 |
±1.3 |
±1.4 |
±1.4 |
±1.6 |
±1.7 |
±1.8 |
160~<200 |
±1.6 |
±1.6 |
±1.7 |
±1.7 |
±1.9 |
±2.0 |
±2.1 |
表3 热轧钢板厚度允许偏差(mm)
厚度 |
宽度 |
||||||
<1000 |
1000~ <1250 |
1250~ <1600 |
1600~ <2000 |
2000~ <2500 |
2500~ <3150 |
3150~ <4000 |
|
2.50~<3.15 |
+0.25 |
+0.35 |
+0.45 |
— |
— |
— |
— |
3.15~<4.00 |
+0.35 |
+0.45 |
-0.55 |
— |
— |
— |
— |
4.00~<5.00 |
+0.51 |
+0.55 |
+0.65 |
+0.95 |
+1.35 |
+1.75 |
— |
5.00~<6.00 |
+0.65 |
+0.65 |
+0.75 |
+1.15 |
+1.55 |
+1.95 |
— |
6.00~<8.00 |
-0.85 |
+0.95 |
+0.95 |
+1.25 |
+1.75 |
+2.15 |
+2.55 |
8.00~<10.0 |
+1.05 |
+1.05 |
+1.05 |
+1.35 |
+2.15 |
+2.75 |
+2.95 |
10.0~<16.0 |
+1.15 |
+1.15 |
+1.15 |
+1.45 |
+2.15 |
+2.75 |
+2.95 |
16.0~<25.0 |
-1.35 |
+1.35 |
+1.35 |
+1.65 |
+2.35 |
+2.75 |
+2.95 |
25.0~<40.0 |
+1.55 |
+1.55 |
+1.55 |
+1.95 |
+2.35 |
+2.75 |
+2.95 |
40.0~<63.0 |
+1.75 |
+1.75 |
+2.15 |
+2.15 |
+2.55 |
+2.75 |
+2.95 |
63.0~<100 |
+1.95 |
+2.15 |
+2.35 |
+2.35 |
+2.75 |
+2.95 |
+3.15 |
100~<160 |
+2.35 |
+2.35 |
+2.55 |
+2.55 |
+2.95 |
+3.15 |
+3.35 |
160~<200 |
+2.95 |
+2.95 |
+3.15 |
+3.15 |
+3.55 |
+3.75 |
+3.95 |
使用表3计算钢板重量时,表示钢板的厚度值应加上表4的数值。
表4 用作计算重量的增加值(mm)
厚度 |
宽度 |
||||||
<1000 |
1000~ <1250 |
1250~ <1600 |
1600~ <2000 |
2000~ <2500 |
2500~ <3150 |
3150~ <4000 |
|
2.50~<3.15 |
0 |
0.05 |
0.10 |
— |
— |
— |
— |
3.15~<4.00 |
0.05 |
0.10 |
0.15 |
— |
— |
— |
— |
4.00~<5.00 |
0.13 |
0.15 |
0.20 |
0.35 |
0.55 |
0.75 |
— |
5.00~<6.00 |
0.20 |
0.20 |
0.25 |
0.45 |
0.65 |
0.85 |
— |
6.00~<8.00 |
0.30 |
0.35 |
0.35 |
0.50 |
0.75 |
0.95 |
1.15 |
8.00~<10.0 |
0.40 |
0.40 |
0.40 |
0.55 |
0.95 |
1.25 |
1.35 |
10.0~<16.0 |
0.45 |
0.45 |
0.45 |
0.60 |
0.95 |
1.25 |
1.35 |
16.0~<25.0 |
0.55 |
0.55 |
0.55 |
0.70 |
1.05 |
1.25 |
1.35 |
25.0~<40.0 |
0.65 |
0.65 |
0.65 |
0.85 |
1.05 |
1.25 |
1.35 |
40.0~<63.0 |
0.75 |
0.75 |
0.95 |
0.95 |
1.15 |
1.25 |
1.35 |
63.0~<100 |
0.85 |
0.95 |
1.05 |
1.05 |
1.25 |
1.35 |
1.45 |
100~<160 |
1.05 |
1.05 |
1.15 |
1.15 |
1.35 |
1.45 |
1.55 |
160~<200 |
1.35 |
1.35 |
1.45 |
1.15 |
1.65 |
1.75 |
1.85 |
冷轧钢板的厚度允许偏差,见表4和表5,表5只有当需方指明要求时才适用。
表5 冷轧钢板厚度允许偏差(mm)
厚度 |
宽度 |
|
<1250 |
1250~<1600 |
|
0.30~<0.60 |
±0.05 |
±0.08 |
0.60~<0.80 |
±0.07 |
±0.09 |
0.80~<1.00 |
±0.09 |
±0.10 |
1.00~<1.25 |
±0.10 |
±0.12 |
1.25~<1.60 |
±0.12 |
±0.15 |
1.60~<2.00 |
±0.15 |
±0.17 |
2.00~<2.50 |
±0.17 |
±0.20 |
2.50~<3.15 |
±0.22 |
±0.25 |
3.15~<4.00 |
±0.25 |
±0.30 |
4.00~<5.00 |
±0.35 |
±0.40 |
5.00~<6.00 |
±0.40 |
±0.45 |
6.00~<8.00 |
±0.50 |
±0.50 |
8.00~<10.0 |
±0.60 |
±0.60 |
10.0~<16.0 |
±0.70 |
±0.70 |
16.0~<25.0 |
±0.80 |
±0.80 |
表6 冷轧钢板厚度允许偏差(mm)
厚度 |
宽度 |
|||||
<160 |
160~ <250 |
250~ <400 |
400~ <630 |
630~ <1000 |
1000~ <1250 |
|
<0.10 |
±0.010 |
±0.020 |
— |
— |
— |
— |
0.10~<0.16 |
±0.015 |
±0.020 |
— |
— |
— |
— |
0.16~<0.25 |
±0.020 |
±0.025 |
±0.030 |
±0.030 |
— |
— |
0.25~<0.40 |
±0.025 |
±0.030 |
±0.035 |
±0.035 |
±0.038 |
±0.038 |
0.40~<0.60 |
±0.035 |
±0.040 |
±0.040 |
±0.040 |
±0.040 |
±0.040 |
0.60~<0.80 |
±0.040 |
±0.045 |
±0.045 |
±0.045 |
±0.05 |
±0.05 |
0.80~<1.00 |
±0.040 |
±0.05 |
±0.05 |
±0.05 |
±0.05 |
±0.06 |
1.00~<1.25 |
±0.05 |
±0.05 |
±0.05 |
±0.05 |
±0.06 |
±0.07 |
1.25~<1.60 |
±0.05 |
±0.06 |
±0.06 |
±0.06 |
±0.07 |
±0.08 |
1.60~<2.00 |
±0.06 |
±0.07 |
±0.08 |
±0.08 |
±0.09 |
±0.10 |
2.00~<2.50 |
±0.07 |
±0.08 |
±0.08 |
±0.09 |
±0.10 |
±0.11 |
2.50~<3.15 |
±0.08 |
±0.09 |
±0.09 |
±0.10 |
±0.12 |
±0.12 |
3.15~<4.00 |
±0.09 |
±0.10 |
±0.10 |
±0.11 |
±0.12 |
±0.13 |
钢板宽度允许偏差,剪切边钢板见表7,轧制边钢板见表8。根据需方要求,冷轧钢板的宽度允许偏差,町以按表9(符号EW)规定
表7 剪切边钢板宽度允许偏差(mm)
切断方法 |
厚度 |
宽度 |
<2000 |
≥2000 |
||||
长度 |
≤3500 |
>3500 ~6000 |
>6000 |
≤3500 |
>3500 ~6000 |
>6000 |
||
机械切断 |
<10.0 |
+5 0 |
+15 0 |
+20 0 |
+15 0 |
+15 0 |
+25 0 |
|
10.~<20.0 |
+10 0 |
+20 0 |
+20 0 |
+20 0 |
+20 0 |
+25 0 |
||
20.0~<28.0 |
+15 0 |
+20 0 |
+20 0 |
+20 0 |
+20 0 |
+25 0 |
||
火焰切断 |
2.50~<100 |
+5 ~+30 |
+5 ~+45 |
+5 ~+55 |
+5 ~+45 |
+5 ~+50 |
+5 ~+60 |
|
100~<200 |
+5 ~+60 |
+5 ~+60 |
+5 ~+60 |
+5 ~+60 |
+5 ~+60 |
+5 ~+60 |
表8 轧制边钢板的宽度允许偏差(mm)
宽度 |
由轧制边钢带剪切的钢板 |
轧制状态钢板 |
<100 |
±1 |
— |
100~<250 |
±2 |
— |
250~<400 |
±5 |
+不定规 0 |
400~<630 |
+20 0 |
+不定规 0 |
630~<1000 |
+25 0 |
+不定规 0 |
≥1000 |
+30 0 |
+不定规 0 |
表9 冷轧钢板宽度允许偏差(符号EW)(mm)
厚度 |
宽度 |
||||
<160 |
160~ <250 |
250~ <400 |
400~ <630 |
630~ <1000 |
|
<0.06 |
±0.15 |
±0.20 |
±0.25 |
±0.30 |
±0.50 |
0.06~<1.00 |
±0.20 |
±0.25 |
±0.25 |
±0.30 |
±0.50 |
1.00~<1.60 |
±0.20 |
±0.30 |
±0.30 |
±0.40 |
±0.60 |
1.60~<2.50 |
±0.35 |
±0.35 |
±0.35 |
±0.50 |
±0.70 |
2.50~<4.00 |
±0.30 |
±0.40 |
±0.40 |
±0.50 |
±0.80 |
钢板长度允许偏差,见表10。
表10 钢扳长度允许偏差(mm)
切断方法 |
厚度 |
长度 |
≤3500 |
>3500~6000 |
>6000 |
|||
宽度 |
<2000 |
≥2000 |
<2000 |
≥2000 |
<2000 |
≥2000 |
||
机械切断 |
<10.0 |
+10 0 |
+15 0 |
+15 0 |
+20 0 |
+30 0 |
+35 0 |
|
10.~<20.0 |
+15 0 |
+20 0 |
+20 0 |
+25 0 |
+35 0 |
+40 0 |
||
20.0~<28.0 |
+15 0 |
+20 0 |
+20 0 |
+25 0 |
+35 0 |
+40 0 |
||
火焰切断 |
2.50~<100 |
+5 ~+30 |
+5 ~+45 |
+5 ~+45 |
+5 ~+50 |
+5 ~+60 |
+5 ~+60 |
|
100~<200 |
+5 ~+60 |
+5 ~+60 |
+5 ~+60 |
+5 ~+60 |
+5 ~+60 |
+5 ~+60 |
钢板的不平度,见表11,根据需方要求,可以使用符号EF的不平度要求。
表11 钢扳不平度最大值
宽度 |
长度 |
不平度最大值 |
不平度最大值 (符号EF) |
≤1000 |
≤2000 |
15 |
3 |
>2000 |
20 |
6 |
|
>1000~1600 |
≤2000 |
20 |
6 |
>2000 |
20 |
6 |
|
>1600~2000 |
≤2000 |
25 |
— |
>2000 |
35 |
— |
|
>2000~2500 |
>2000 |
40 |
— |
>2500~3150 |
>2500 |
45 |
— |
>3150 |
>3150 |
50 |
— |
注:①表11适用于任意3500mm长度,长度小于3500mm,适用于全长。
②适用于从轧制边钢带切取的钢板及剪切边钢板。
钢带的形状、尺寸及允许偏差,按JIS G 4304或JIS G 4305的有关规定。
外观要求
钢板不应有对使用有害的缺陷。
钢带,因为一般没有去除缺陷的机会,可以含有若干不正常的部分。
热处理
钢板经热轧或冷轧后,按表12或表13进行热处理,进行酸洗或类似处理之后,必要时应进行进当的矫直。根据供需双方协议,也可以省去酸洗等处理,而对SUH660和SUH661,需方应指明热处理的种类,更要明确是对钢板本体还是对试样热处理。
为了获得规定的力学性能,必要时生产厂可队改变表12和表13的温度范围的上限。
热处理的符号见表14。
表12 奥氏体钢的热处理
牌号 |
热处理,℃ |
|
固溶处理 |
时效处理 |
|
SUH309 SUH310 SUH330 SUH660 SUH661 |
1030~1150急冷 1030~1180急冷 1030~1180急冷 965~995急冷 1130~1200急冷 |
760~760×16h空冷或徐冷 780~830×4h空冷或徐冷 |
表13 铁素体钢的热处理
牌号 |
退火,℃ |
SUH21 |
780~950急冷或徐冷 |
SUH409 |
780~950急冷或徐冷 |
SUH |
780~950急冷或徐冷 |
SUH446 |
780~880急冷 |
表14 热处理符号
热处理方法 |
符合 |
固溶处理 |
S |
固溶处理后时效处理 |
H |