低碳钢热轧盘条
低碳钢热轧盘条牌号和化学成分（GB701－1997）
|
牌号 |
化学成分％ |
脱氧方法 |
||||
|
C |
Si |
Mn |
P |
S |
||
|
不 大 于 |
||||||
|
Q195 |
0.06－0.12 |
0.25－0.50 |
0.3 |
≤0.045 |
≤0.050 |
F、B、Z |
|
Q |
≤ 0.10 |
0.30－0.60 |
≤0.040 |
≤0.040 |
||
|
Q |
0.09－0.15 |
0.25－0.55 |
0.3 |
0.045 |
≤0.050 |
F、B、Z |
|
Q215B |
0.04 |
≤0.045 |
||||
|
Q |
0.10－0.15 |
0.30－0.60 |
0.04 |
≤0.040 |
||
|
Q |
0.14－0.22 |
0.30－0.65 |
0.3 |
0.045 |
≤0.050 |
F、B、Z |
|
Q235B |
0.12－0.20 |
0.30－0.70 |
≤0.045 |
|||
|
Q |
≤ 0.18 |
0.30－0.60 |
≤0.040 |
≤0.040 |
||
优质碳素结构钢无扭控冷热轧盘条（GB699－1999）
|
统一数字代号 |
牌号 |
牌号 |
|||||
|
C |
Si |
Mn |
Cr |
Ni |
Cu |
||
|
不大于 |
|||||||
|
U20082 |
8 |
0.05-0.11 |
0.17-0.37 |
0.35-0.65 |
0.1 |
0.3 |
0.25 |
|
U20102 |
10 |
0.07-0.13 |
0.17-0.37 |
0.35-0.65 |
0.15 |
0.3 |
0.25 |
|
U20152 |
15 |
0.12-0.18 |
0.17-0.37 |
0.35-0.65 |
0.25 |
0.3 |
0.25 |
|
U20202 |
20 |
0.17-0.23 |
0.17-0.37 |
0.35-0.65 |
0.25 |
0.3 |
0.25 |
|
U20252 |
25 |
0.22-0.29 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20302 |
30 |
0.27-0.34 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20352 |
35 |
0.32-0.39 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20402 |
40 |
0.37-0.44 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20452 |
45 |
0.42-0.50 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20502 |
50 |
0.47-0.55 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20552 |
55 |
0.52-0.60 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20602 |
60 |
0.57-0.65 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20652 |
65 |
0.62-0.70 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20702 |
70 |
0.67-0.75 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20752 |
75 |
0.72-0.80 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20802 |
80 |
0.77-0.85 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20852 |
85 |
0.82-0.90 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.3 |
0.25 |
|
U20152 |
15Mn |
0.12-0.18 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.3 |
0.25 |
|
U20202 |
20Mn |
0.17-0.23 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.3 |
0.25 |
|
U20252 |
25Mn |
0.22-0.29 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.3 |
0.25 |
|
U20302 |
30Mn |
0.27-0.34 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.3 |
0.25 |
|
U20352 |
35Mn |
0.32-0.39 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.3 |
0.25 |
|
U20402 |
40Mn |
0.37-0.44 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.3 |
0.25 |
|
U20452 |
45Mn |
0.42-0.50 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.3 |
0.25 |
|
U20502 |
50Mn |
0.48-0.56 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.3 |
0.25 |
|
U20552 |
55Mn |
0.52-0.60 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.3 |
0.25 |
|
U20602 |
60Mn |
0.57-0.65 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.3 |
0.25 |
|
U20652 |
65Mn |
0.62-0.70 |
0.17-0.37 |
0.90-1.20 |
0.25 |
0.3 |
0.25 |
|
U20702 |
70Mn |
0.67-0.75 |
0.17-0.37 |
0.90-1.20 |
0.25 |
0.3 |
0.25 |
表中所列牌号为优质钢，如果是高级优质钢，在牌号后加“A”(统一数字代号最后一位数字改为“3”)；如果是特级优质钢在牌号后加“E”(统一数字代号最后一位数字改为“6”)；对于沸腾钢牌号后加“F”(统一数字代号最后一位数字改为“0”)；对于半镇定钢牌号后加 “b”(统一数字代号最后一位数字改为“1”)。
|
组别 |
P |
S |
|
不大于,% |
||
|
优质钢 |
0.035 |
0.035 |
|
高级优质钢 |
0.03 |
0.03 |
|
0.025 |
0.025 |
0.025 |
产品用途：用于制绳钢丝和钢线使用。