创建时间:2008-08-02
合金 |
TB/℃ |
铸锭 |
锻坯 |
||
开坯温度/℃ |
终锻温度/℃ |
始锻温度/℃ |
终锻温度/℃ |
||
TA2,TA3 |
890~920 |
1050 |
750 |
950 |
650 |
TA7 |
930~970 |
1180 |
900 |
1100 |
850 |
TB2 |
730~70 |
1100 |
|
可冷加工 |
|
Ti-1023 |
790~820 |
950 |
750 |
850 |
700 |
TC1 |
920~930 |
980 |
750 |
900 |
700 |
TC3 |
940~990 |
1050 |
850 |
920 |
800 |
TC4 |
980~1010 |
1150 |
850 |
980 |
800 |
TC5 |
930~980 |
1150 |
750 |
950 |
800 |
TC6 |
960~1000 |
1150 |
850 |
950 |
800 |
TC8 |
970~1000 |
1150 |
900 |
970 |
850 |
TC9 |
970~1000 |
1150 |
900 |
970 |
850 |
TC10 |
930~960 |
1150 |
900 |
930 |
850 |
TC11 |
980~1020 |
1200 |
900 |
980 |
850 |