收藏词条 编辑词条 铸造中按H8与H7级精度加工已预先铸出或热冲出的孔的余量
按H8与H7级精度加工已预先铸出或热冲出的孔的余量(单位:mm)
加工孔的直径 |
直径 |
加工孔的直径 |
直径 |
||||||||
粗镗 |
半精镗 |
粗铰或一次半精镗 |
精铰或精镗 |
粗镗 |
半精镗 |
粗铰或一次半精镗 |
精铰或精镗 |
||||
第一次 |
第二次 |
第一次 |
第二次 |
||||||||
30 |
— |
28 |
29.8 |
29.93 |
30 |
105 |
100 |
103 |
104.3 |
104.8 |
105 |
32 |
— |
30 |
31.7 |
31.93 |
32 |
110 |
105 |
108 |
109.3 |
109.8 |
110 |
35 |
— |
33 |
34.7 |
34.93 |
35 |
115 |
110 |
113 |
114.3 |
114.8 |
115 |
38 |
— |
36 |
37.7 |
37.93 |
38 |
120 |
115 |
118 |
119.3 |
119.8 |
120 |
40 |
— |
38 |
39.7 |
39.93 |
40 |
125 |
120 |
123 |
124.3 |
124.8 |
125 |
42 |
— |
40 |
41.7 |
41.93 |
42 |
130 |
125 |
128 |
129.3 |
129.8 |
130 |
45 |
— |
43 |
44.7 |
44.93 |
45 |
135 |
130 |
133 |
134.3 |
134.8 |
135 |
48 |
— |
46 |
47.7 |
47.93 |
48 |
140 |
135 |
138 |
139.3 |
139.8 |
140 |
50 |
45 |
48 |
49.7 |
49.93 |
50 |
145 |
140 |
143 |
144.3 |
144.8 |
145 |
52 |
47 |
50 |
51.7 |
51.93 |
52 |
150 |
145 |
148 |
149.3 |
149.8 |
150 |
55 |
51 |
53 |
54.5 |
54.92 |
55 |
155 |
150 |
153 |
154.3 |
154.8 |
155 |
58 |
54 |
56 |
57.5 |
57.92 |
58 |
160 |
155 |
158 |
159.3 |
159.8 |
160 |
60 |
56 |
58 |
59.5 |
59.95 |
60 |
165 |
160 |
163 |
164.3 |
164.8 |
165 |
62 |
58 |
60 |
61.5 |
61.92 |
62 |
170 |
165 |
168 |
169.3 |
169.8 |
170 |
65 |
61 |
63 |
64.5 |
64.92 |
65 |
175 |
170 |
173 |
174.3 |
174.8 |
175 |
68 |
64 |
66 |
67.5 |
67.9 |
68 |
180 |
175 |
178 |
179.3 |
179.8 |
180 |
70 |
66 |
68 |
69.5 |
69.9 |
70 |
185 |
180 |
183 |
184.3 |
184.8 |
185 |
72 |
68 |
70 |
71.5 |
71.9 |
72 |
190 |
185 |
188 |
189.3 |
189.8 |
190 |
75 |
71 |
73 |
74.5 |
74.9 |
75 |
195 |
190 |
193 |
194.3 |
194.8 |
195 |
78 |
74 |
76 |
77.5 |
77.9 |
78 |
200 |
194 |
197 |
199.3 |
199.8 |
200 |
80 |
75 |
78 |
79.5 |
79.9 |
80 |
210 |
204 |
207 |
209.3 |
209.8 |
210 |
82 |
77 |
80 |
81.3 |
81.85 |
82 |
220 |
214 |
217 |
219.3 |
219.8 |
220 |
85 |
80 |
83 |
84.3 |
84.85 |
85 |
250 |
244 |
247 |
249.3 |
249.8 |
250 |
88 |
83 |
86 |
87.3 |
87.85 |
88 |
280 |
274 |
277 |
279.3 |
279.8 |
280 |
90 |
85 |
88 |
89.3 |
89.85 |
90 |
300 |
294 |
297 |
299.3 |
299.8 |
300 |
92 |
87 |
90 |
91.3 |
91.85 |
92 |
320 |
314 |
317 |
319.3 |
319.8 |
320 |
95 |
90 |
93 |
94.3 |
94.85 |
95 |
350 |
342 |
347 |
349.3 |
349.8 |
350 |
98 |
93 |
96 |
97.3 |
97.85 |
98 |
380 |
372 |
377 |
379.2 |
379.75 |
380 |
100 |
93 |
98 |
99.3 |
99.85 |
100 |
400 |
392 |
397 |
399.2 |
399.75 |
400 |
注:1、如果铸出的孔有很大的加工余量时,则第一次粗镗可分为两次或多次粗镗。
2、如果只进行一次半精镗,则其加工余量为表中“半精镗”和“粗铰或二次半精镗”加工余量之和。