牌号 |
化学成分(质量分数)/% |
||||||||
C≤ |
Si |
Mn≤ |
P≤ |
S≤ |
Cr |
Mo |
Ni |
Ti |
|
PN/H 83158 不锈钢 |
|||||||||
L0H12N |
|
|
|
0.035 |
0.035 |
|
≤1.00 |
3.50~5.00 |
|
L0H13 |
0.08 |
0.70 |
0.40~0.80 |
0.035 |
0.035 |
12.0~14.0 |
|
≤1.00 |
|
L0H18N |
0.07 |
2.00 |
2.00 |
0.035 |
0.035 |
17.0~19.0 |
≤0.50 |
8.00~11.0 |
|
L0N18N |
0.07 |
2.00 |
2.00 |
0.035 |
0.035 |
17.0~19.0 |
2.00~2.50 |
9.00~11.0 |
|
LH14 |
0.15~0.30 |
0.70 |
0.40~0.80 |
0.035 |
0.035 |
12.0~15.0 |
|
≤1.00 |
|
LH14N |
0.15 |
0.60 |
0.40~0.90 |
0.035 |
0.035 |
12.0~15.0 |
|
0.70~1.20 |
|
LH16N |
0.20 |
1.00~2.00 |
6.00~7.00 |
0.035 |
0.035 |
15.0~17.0 |
|
4.50~5.50 |
|
LH17N |
0.25 |
1.50 |
1.50 |
0.035 |
0.035 |
16.5~18.5 |
|
7.50~8.50 |
|
LH17N37S |
0.20~0.50 |
1.00~2.50 |
1.50 |
0.035 |
0.035 |
15.0~19.0 |
|
34.0~39.0 |
|
LH18N9 |
0.15 |
2.00 |
2.00 |
0.035 |
0.035 |
17.0~19.0 |
|
8.00~11.0 |
|
LH18N9T |
0.15 |
2.00 |
2.00 |
0.035 |
0.035 |
17.0~19.0 |
|
8.00~11.0 |
5×(C~0.03)~0.80 |
LH18N |
0.15 |
2.00 |
2.00 |
0.035 |
0.035 |
17.0~19.0 |
2.00~2.50 |
9.00~11.0 |
|
LH18N |
0.15 |
2.00 |
2.00 |
0.035 |
0.035 |
17.0~19.0 |
2.00~2.50 |
9.00~11.0 |
5×(C~0.03)~0.80 |
LH21N5 |
0.12 |
1.50 |
2.00 |
0.035 |
0.035 |
20.0~22.0 |
|
4.50~6.00 |
|
LH21N |
0.12 |
1.50 |
2.00 |
0.035 |
0.035 |
20.0~22.0 |
1.80~2.20 |
4.50~6.00 |
|
LH21N5T |
0.12 |
1.50 |
2.00 |
0.035 |
0.035 |
20.0~22.0 |
|
4.50~6.00 |
5×C~0.70 |
LH26N4S2 |
0.20 |
2.50 |
0.80 |
0.035 |
0.030 |
24.0~28.0 |
|
3.00~5.00 |
|
PN/H 83159 耐热钢 |
|||||||||
LH17N |
0.26 |
1.50 |
1.50 |
0.040 |
0.035 |
16.5~18.5 |
|
7.50~8.50 |
|
LH17N37S |
0.20~0.50 |
1.00~2.50 |
1.50 |
0.035 |
0.035 |
15.0~19.0 |
|
34.0~39.0 |
|
LH18S2 |
1.35~1.50 |
1.90~2.50 |
0.40 |
0.040 |
0.035 |
17.0~19.0 |
|
|
|
LH19N |
0.25 |
1.50 |
1.00 |
0.040 |
0.035 |
18.0~20.0 |
|
13.0~15.0 |
|
LH23N |
0.25 |
1.80 |
1.50 |
0.040 |
0.035 |
22.0~24.0 |
|
16.5~18.5 |
|
LH25N19S2 |
0.25 |
2.00~3.00 |
0.60 |
0.040 |
0.035 |
24.0~26.0 |
|
17.5~19.5 |
|
LH26 |
0.40~0.60 |
1.00 |
0.80 |
0.040 |
0.035 |
25.0~27.0 |
|
|
|
LH26N4S2 |
0.20 |
2.50 |
0.80 |
0.035 |
0.030 |
24.0~28.0 |
|
3.00~5.00 |
|
LH29S2 |
1.45~1.60 |
1.50~2.10 |
1.00 |
0.040 |
0.035 |
28.0~30.0 |
|
|
|