压力容器用碳钢锻件
JIS G3202 表1
牌 号 |
化学成分(质量分数)/% |
||||
C ≤ |
Si ≤ |
Mn |
P ≤ |
S ≤ |
|
SFVC 1 SFVC SFVC 2 B |
0.30 0.35 0 40~1.35 0.030 0.030 0.35 0.35 0 40~1.10 0.030 0.030 0.30 0.35 0.70~1.35 0.030 0.030 |
压力容器用合金钢锻件
牌 号 |
化学成分(质量分数)/% |
||||||
C ≤ |
Si ≤ |
Mn |
P ≤ |
S ≤ |
Cr |
Mo |
|
SFVA F1 SFVA F2 SFVA F SFVA F5B SFVA F SFVA F5D SFVA F9 SFVA F SFVA F11B SFVA F12 SFVA F SFVA F21B SFVA F SFVA F22B |
0.30 0.35 0.60~0.90 0.030 0.030 0.45~0.65 0.20 0.60 0.30~0.80 0.030 0.030 0.50~0.80 0.45~0.65 0.15 0.50 0.30~0.60 0.030 0.030 4.00~6.00 0.45~0.65 0.15 0.50 0.30~0.60 0.030 0.030 4.00~6.00 0.45~0.65 0.25 0.50 0.30~0.60 0.030 0.030 4.00~6.00 0.45~0.65 0.25 0.50 0.30~0.60 0.030 0.030 4.00~6.00 0.45~0.65 0.15 0.50~1.00 0.30~0.60 0.030 0.030 8.00~10.0 0.90~1.10 0.20 0.50~1.00 0.30~0.80 0.030 0.030 1.00~1.50 0.45~0.65 0.20 0.50~1.00 0.30~0.80 0.030 0.030 1.00~1.50 0.45~0.65 0.20 0.60 0.30~0.80 0.030 0.030 0.80~1 25 0.45~0.65 0.15 0.50 0.30~0.60 0.030 0.030 2.65~3.35 0.80~1.00 0.15 0.50 0.30~0.60 0.030 0.030 2.65~3.35 0.80~1.00 0.15 0.50 0.30~0.60 0.030 0.030 2.00~2.50 0.90~1.10 0.15 0.50 0.30~0.60 0.030 0.030 2.00~2.50 0.90~1.10 |
压力容器用调质型台金钢锻件
JIS G3204 表3
牌 号 |
化学成分(质量分数)/% |
||||||||
C ≤ |
Si ≤ |
Mn |
P ≤ |
S ≤ |
Cr |
Mo |
Ni |
V ≤ |
|
SFVQ |
0.25 |
0.40 |
1.20~1.50 |
0.030 |
0.03 |
≤0.25 |
0.45~0.60 |
0.40~1.00 |
0.05 |
SFVQ 1 B |
0.25 |
0.40 |
1.20~1.50 |
0.030 |
0.03 |
≤0.25 |
0.45~0.60 |
0.40~1.00 |
0.05 |
SFVQ |
0.27 |
0.40 |
0.50~1.00 |
0.030 |
0.03 |
0.25~0.45 |
0.55~0.70 |
0.50~1.00 |
0.05 |
SFVQ 2 B |
0.27 |
0.40 |
0.50~1.00 |
0.030 |
0.03 |
0.25~0.45 |
0.55~0.70 |
0.50~1.00 |
0.05 |
SFVQ 3 |
0 23 |
0.40 |
0.20~0.40 |
0.020 |
0.02 |
1.50~2.00 |
0.40~0.60 |
2.75~3.90 |
0.03 |
高温压力容器用锻件
JIS G3206 表4
牌号 |
化学成分(质量分数)/% |
|||||||
C ≤ |
Si ≤ |
Mn |
P ≤ |
S ≤ |
Cr |
Mo |
V |
|
SFVCM F22B |
0.170 |
0.500 |
0.30~0.60 |
0.015 |
0.015 |
2.00~2.50 |
0.90~1.10 |
≤0.03 |
SFVCM F22V |
0.170 |
0.100 |
0.30~0.60 |
0.015 |
0.010 |
2.00~2.50 |
0.90~1.10 |
0.25~0.35 |
SFVCM F3V |
0.170 |
0.100 |
0.30~0.60 |
0.015 |
0.010 |
2.75~3.25 |
0.90~1.10 |
0.20~0.30 |