1 熔化焊用钢丝
适用于电弧焊、埋弧自动焊和半自动焊、电渣焊和气焊等用途。钢丝直径1.6~6.0mm。钢丝化学成分见表一。
GB/T 14957 表一
钢种 |
牌号 |
化学成分(质量分数)/% |
||||||||||
C |
Si |
Mn |
S<= |
P<= |
Cr |
Mo |
Ni |
V |
Cu<= |
其它 |
||
碳素结构钢 |
H |
<=0.1 |
<=0.03 |
0.3-0.55 |
0.03 |
0.03 |
<=0.02 |
|
<=0.3 |
|
0.2 |
|
H08E |
<=0.1 |
<=0.03 |
0.3-0.55 |
0.02 |
0.02 |
<=0.02 |
|
<=0.3 |
|
0.2 |
|
|
H |
<=0.1 |
<=0.03 |
0.3-0.55 |
0.015 |
0.015 |
<=0.01 |
|
<=0.1 |
|
0.2 |
|
|
H08MnA |
<=0.1 |
<=0.07 |
0.8-1.1 |
0.03 |
0.03 |
<=0.02 |
|
<=0.3 |
|
0.2 |
|
|
H |
0.11-0.18 |
<=0.03 |
0.35-0.65 |
0.03 |
0.03 |
<=0.02 |
|
<=0.3 |
|
0.2 |
|
|
H15Mn |
0.11-0.18 |
<=0.03 |
0.8-1.1 |
0.035 |
0.035 |
<=0.02 |
|
<=0.3 |
|
0.2 |
|
|
合金结构钢 |
H10Mn2 |
<=0.12 |
<=0.07 |
1.5-1.9 |
0.035 |
0.035 |
<=0.2 |
|
<=0.3 |
|
0.2 |
|
H08Mn2Si |
<=0.11 |
0.65-0.95 |
1.7-2.1 |
0.035 |
0.035 |
<=0.2 |
|
<=0.3 |
|
0.2 |
|
|
H08Mn2SiA |
<=0.11 |
0.65-0.95 |
1.8-2.1 |
0.03 |
0.03 |
<=0.2 |
|
<=0.3 |
|
0.2 |
|
|
H10MnSi |
<=0.14 |
0.6-0.9 |
0.8-1.1 |
0.035 |
0.035 |
<=0.2 |
|
<=0.3 |
|
0.2 |
|
|
H10MnSiMo |
<=0.14 |
0.7-1.1 |
0.9-1.2 |
0.035 |
0.035 |
<=0.2 |
0.15-0.25 |
<=0.3 |
|
0.2 |
|
|
H10MnSiMoTiA |
0.08-0.12 |
0.4-0.7 |
1-1.3 |
0.025 |
0.03 |
<=0.2 |
0.2-0.4 |
<=0.3 |
|
0.2 |
Ti0.05-0.15 |
|
H08MnMoA |
<=0.1 |
<=0.25 |
1.2-1.6 |
0.03 |
0.03 |
<=0.2 |
0.3-0.5 |
<=0.3 |
|
0.2 |
Ti0.15(加入量) |
|
H08Mn2MoA |
0.06-0.11 |
<=0.25 |
1.6-1.9 |
0.03 |
0.03 |
<=0.2 |
0.5-0.7 |
<=0.3 |
|
0.2 |
Ti0.15(加入量) |
|
H10Mn2MoA |
0.08-0.13 |
<=0.4 |
1.7-2 |
0.03 |
0.03 |
<=0.2 |
0.6-0.8 |
<=0.3 |
|
0.2 |
Ti0.15(加入量) |
|
H08Mn2MoVA |
0.06-0.11 |
<=0.25 |
1.6-1.9 |
0.03 |
0.03 |
<=0.2 |
0.5-0.7 |
<=0.3 |
0.06-0.12 |
0.2 |
Ti0.15(加入量) |
|
H10Mn2MoVA |
0.08-0.13 |
<=0.4 |
1.7-2 |
0.03 |
0.03 |
<=0.2 |
0.6-0.8 |
<=0.3 |
0.06-0.12 |
0.2 |
Ti0.15(加入量) |
|
H08CrMoA |
<=0.1 |
0.15-0.35 |
0.4-0.7 |
0.03 |
0.03 |
0.8-1.1 |
0.4-0.6 |
<=0.3 |
|
0.2 |
|
|
H13CrMoA |
0.11-0.16 |
0.15-0.35 |
0.4-0.7 |
0.03 |
0.03 |
0.8-1.1 |
0.4-0.6 |
<=0.3 |
|
0.2 |
|
|
H18CrMoA |
0.15-0.22 |
0.15-0.35 |
0.4-0.7 |
0.025 |
0.03 |
0.8-1.1 |
0.15-0.25 |
<=0.3 |
|
0.2 |
|
|
H08CrMoVA |
<=0.1 |
0.15-0.35 |
0.4-0.7 |
0.03 |
0.03 |
1-1.3 |
0.5-0.7 |
<=0.3 |
0.15-0.35 |
0.2 |
|
|
H08CrNi2MoA |
0.05-0.1 |
0.1-0.3 |
0.5-0.85 |
0.025 |
0.03 |
0.7-1 |
0.2-0.4 |
1.4-1.8 |
|
0.2 |
|
|
H30CrMnSiA |
0.25-0.35 |
0.9-1.2 |
0.8-1.1 |
0.025 |
0.025 |
0.8-1.1 |
|
<=0.3 |
|
0.2 |
|
|
H10MoCrA |
<=0.12 |
0.15-0.35 |
0.4-0.7 |
0.03 |
0.03 |
0.45-0.65 |
0.4-0.6 |
<=0.3 |
|
0.2 |
|
2 气体保护焊用钢丝
用于低碳钢、低合金钢和台金钢用气焊保护焊(C02、C02+02,C02+Ar)。钢丝直径0.6~2.2mm。钢丝化学成分见表二。
GB/T l4958 表二
牌号 |
化学成分(质量分数)/% |
|||||||||
C |
Si |
Mn |
P<= |
S<= |
Cr<= |
Mo<= |
Ni<= |
Cu<= |
V<= |
|
H08MnSi |
<=0.11 |
0.4-0.7 |
1.2-1.5 |
0.035 |
0.035 |
0.2 |
|
0.3 |
0.2 |
|
H08Mn2Si |
<=0.11 |
0.65-0.95 |
1.7-2.1 |
0.035 |
0.035 |
0.2 |
|
0.3 |
0.2 |
|
H08Mn2SiA |
<=0.11 |
0.65-0.95 |
1.8-2.1 |
0.03 |
0.03 |
0.2 |
|
0.3 |
0.2 |
|
H11MnSi |
0.07-0.15 |
0.65-0.95 |
1-1.5 |
0.025 |
0.035 |
|
0.15 |
0.15 |
|
0.05 |
H11Mn2SiA |
0.07-0.15 |
0.85-1.15 |
1.4-1.85 |
0.025 |
0.025 |
|
0.15 |
0.15 |
|
0.05 |
3 焊接用不锈钢丝
适用于电弧焊、气焊、埋弧自动焊、电渣焊和气体保护焊用钢丝。钢丝直径不大于l0mm。钢丝化学成分见表三。
YB/T 5092 表三
类别 |
牌号 |
化学成分(质量分数)/% |
|||||||||
C<= |
Si<= |
Mn |
P<= |
S<= |
Cr |
Mo |
Ni |
Cu |
其它 |
||
奥氏体型 |
H1Cr19Ni9 |
0.14 |
0.6 |
1-2.0 |
0.03 |
0.03 |
18-20 |
|
8-10.0 |
|
|
H0Cr19Ni12Mo2 |
0.08 |
0.6 |
1-2.5 |
0.03 |
0.03 |
18-20 |
2-3.0 |
11-14.0 |
|
|
|
H00Cr19Ni12Mo2 |
0.03 |
0.6 |
1-2.5 |
0.03 |
0.02 |
18-20 |
2-3.0 |
11-14.0 |
|
|
|
H00Cr19Ni12Mo2Cu2 |
0.03 |
0.6 |
1-2.5 |
0.03 |
0.02 |
18-20 |
2-3.0 |
11-14.0 |
1-2.5 |
|
|
H0Cr19Ni14Mo3 |
0.08 |
0.6 |
1-2.5 |
0.03 |
0.03 |
18.5-20.5 |
3-4.0 |
13-15 |
|
|
|
H0Cr21Ni10 |
0.08 |
0.6 |
1-2.5 |
0.03 |
0.03 |
19.5-22 |
|
9-11.0 |
|
|
|
H00Cr21Ni10 |
0.03 |
0.6 |
1-2.5 |
0.03 |
0.02 |
19.5-22 |
|
9-11.0 |
|
|
|
H0Cr20Ni10Ti |
0.08 |
0.6 |
1-2.5 |
0.03 |
0.03 |
18.5-20.5 |
|
9-10.5 |
|
Ti9×C%-1 |
|
H0Cr20Ni10Nb |
0.08 |
0.6 |
1-2.5 |
0.03 |
0.03 |
19-21.5 |
|
9-11.0 |
|
Nb10×C%-1 |
|
H00Cr20Ni25Mo4Cu |
0.03 |
0.6 |
1-2.5 |
0.03 |
0.02 |
19-21 |
4-5.0 |
24-26 |
1-2.0 |
|
|
H1Cr21Ni10Mn6 |
0.1 |
0.6 |
5-7.0 |
0.03 |
0.02 |
20-22 |
|
9-11.0 |
|
|
|
H1Cr24Ni13 |
0.12 |
0.6 |
1-2.5 |
0.03 |
0.03 |
23-25 |
|
12-14.0 |
|
|
|
H1Cr24Ni13Mo2 |
0.12 |
0.6 |
1-2.5 |
0.03 |
0.03 |
23-25 |
2-3.0 |
12-14.0 |
|
|
|
H00Cr25Ni22Mn4Mo2N |
0.03 |
0.5 |
3.5-5.5 |
0.03 |
0.02 |
24-26 |
2-2.8 |
21.5-23 |
|
N0.1-0.15 |
|
H1Cr26Ni21 |
0.15 |
0.6 |
1-2.5 |
0.03 |
0.03 |
25-28 |
|
20-22 |
|
|
|
H0Cr26Ni21 |
0.08 |
0.6 |
1-2.5 |
0.03 |
0.03 |
25-28 |
|
20-22 |
|
|
|
铁素体型 |
H0Cr14 |
0.06 |
0.7 |
<=0.6 |
0.03 |
0.03 |
13-15 |
|
<=0.6 |
|
|
H1Cr17 |
0.1 |
0.5 |
<=0.6 |
0.03 |
0.03 |
15.5-17 |
|
<=0.6 |
|
|
|
马氏体型 |
H1Cr13 |
0.12 |
0.5 |
<=0.6 |
0.03 |
0.03 |
11.5-13.5 |
|
<=0.6 |
|
|
H2Cr13 |
0.13-0.21 |
0.6 |
<=0.6 |
0.03 |
0.03 |
12-14.0 |
|
<=0.6 |
|
|
|
H0Cr17Ni4Cu4Nb |
0.05 |
0.75 |
0.25-0.75 |
0.03 |
0.03 |
15.5-17.5 |
<=0.75 |
4-5.0 |
3-4.0 |
Nb0.15-0.45 |
4 焊接用盘条钢
适用于手工电弧焊、埋弧焊、电渣焊、气焊和气体保护焊等用途的焊接用铜盘条。直径5.5~30mm。盘条化学成分见表四。
GB/T 3429 表四
牌号 |
化学成分(质量分数)/% |
||||||||||
C |
Si |
Mn |
S<= |
P<= |
Cr |
Ni |
Cu |
Mo |
V |
其它 |
|
H |
<=0.1 |
<=0.03 |
0.3-0.6 |
0.03 |
0.03 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H08E |
<=0.1 |
<=0.03 |
0.3-0.6 |
0.02 |
0.02 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H |
<=0.1 |
<=0.03 |
0.3-0.6 |
0.015 |
0.015 |
<=0.1 |
<=0.1 |
<=0.1 |
|
|
|
H08MnA |
<=0.1 |
<=0.07 |
0.8-1.1 |
0.03 |
0.03 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H |
0.11-0.18 |
<=0.03 |
0.35-0.65 |
0.03 |
0.03 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H15Mn |
0.11-0.18 |
<=0.03 |
0.8-1.1 |
0.035 |
0.035 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H08MnSi |
<=0.1 |
0.4-0.7 |
1.2-1.5 |
0.035 |
0.035 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H10MnSi |
<=0.14 |
0.6-0.9 |
0.8-1.1 |
0.035 |
0.035 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H11MnSiA |
0.07-0.15 |
0.65-0.95 |
1-1.5 |
0.025 |
0.035 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H08Mn2Si |
<=0.11 |
0.65-0.95 |
1.7-2.1 |
0.035 |
0.035 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H08Mn2SiA |
<=0.11 |
0.65-0.95 |
1.8-2.1 |
0.03 |
0.03 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H08MnMoA |
<=0.1 |
<=0.25 |
1.2-1.6 |
0.03 |
0.03 |
<=0.2 |
<=0.3 |
<=0.2 |
0.3-0.5 |
|
Ti0.15(加入量) |
H08Mn2MoA |
0.06-0.11 |
<=0.25 |
1.6-1.9 |
0.03 |
0.03 |
<=0.2 |
<=0.3 |
<=0.2 |
0.3-0.5 |
|
Ti0.15(加入量) |
H08Mn2MoVA |
0.06-0.11 |
<=0.25 |
1.6-1.9 |
0.03 |
0.03 |
<=0.2 |
<=0.3 |
<=0.2 |
0.5-0.7 |
0.06-0.12 |
Ti0.15(加入量) |
H08CrMoA |
<=0.1 |
0.15-0.35 |
0.4-0.7 |
0.03 |
0.03 |
0.8-1.1 |
<=0.3 |
<=0.2 |
0.4-0.6 |
|
|
H08CrMoVA |
<=0.1 |
0.15-0.35 |
0.4-0.7 |
0.03 |
0.03 |
1-1.3 |
<=0.3 |
<=0.2 |
0.5-0.7 |
0.15-0.35 |
|
H08CrNi2MoA |
0.05-0.1 |
0.1-0.3 |
0.5-0.85 |
0.025 |
0.03 |
0.7-1 |
1.4-1.8 |
<=0.2 |
0.2-0.4 |
|
|
H10Mn2 |
<=0.12 |
<=0.07 |
1.5-1.9 |
0.035 |
0.035 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H10MnSiMo |
<=0.14 |
0.7-1.1 |
0.9-1.2 |
0.035 |
0.035 |
<=0.2 |
<=0.3 |
<=0.2 |
0.15-0.25 |
|
|
H10MnSiMoTiA |
0.08-0.12 |
0.4-0.7 |
1-1.3 |
0.025 |
0.03 |
<=0.2 |
<=0.3 |
<=0.2 |
0.2-0.4 |
|
Ti0.15-0.15 |
H10Mn2MoA |
0.08-0.13 |
<=0.4 |
1.7-2.00 |
0.03 |
0.03 |
<=0.2 |
<=0.3 |
<=0.2 |
0.6-0.8 |
|
Ti0.15(加入量) |
H10Mn2MoVA |
0.08-0.13 |
<=0.4 |
1.7-2.00 |
0.03 |
0.03 |
<=0.2 |
<=0.3 |
<=0.2 |
0.6-0.8 |
0.06-0.12 |
Ti0.15(加入量) |
H10MoCrA |
<=0.12 |
0.15-0.35 |
0.4-0.7 |
0.03 |
0.03 |
0.45-0.65 |
<=0.3 |
<=0.2 |
0.4-0.6 |
|
|
H11Mn2SiA |
0.07-0.15 |
0.85-1.15 |
1.4-1.85 |
0.025 |
0.025 |
<=0.2 |
<=0.3 |
<=0.2 |
|
|
|
H13CrMoA |
0.11-0.16 |
0.15-0.35 |
0.4-0.7 |
0.03 |
0.03 |
0.8-1.1 |
<=0.3 |
<=0.2 |
0.4-0.6 |
|
|
H18CrMoA |
0.15-0.22 |
0.15-0.35 |
0.4-0.7 |
0.025 |
0.03 |
0.8-1.1 |
<=0.3 |
<=0.2 |
0.15-0.25 |
|
|
H30CrMnSiA |
0.25-0.35 |
0.9-1.2 |
0.8-1.1 |
0.025 |
0.025 |
0.8-1.1 |
<=0.3 |
<=0.2 |
|
|
|