收藏词条 编辑词条 日本高温压力容器用合金钢锻件钢号
创建时间:2008-08-02
JIS G3203
牌号 |
化学成分(质量分数)/% |
||||||
C ≤ |
Si ≤ |
Mn |
P ≤ |
S ≤ |
Cr |
Mo |
|
SFVA F1 |
0.3 |
0.35 |
0.60~0.30 |
≤0.030 |
≤0.030 |
|
0.45~0.65 |
SFVA F2 |
0.2 |
0.60 |
0.30~0.80 |
≤0.030 |
≤0.030 |
0.50~0.80 |
0.45~0.65 |
SFVA F12 |
0.2 |
0.60 |
0.30~0.80 |
≤0.030 |
≤0.030 |
0.80~1.25 |
0.45~0.65 |
SFVA F |
0.2 |
0.50~1.00 |
0.30~0.80 |
≤0.030 |
≤0.030 |
1.00~1.50 |
0.45~0.65 |
SFVA F11B |
|||||||
SFVA F |
0.15 |
0.50 |
0.30~0.60 |
≤0.030 |
≤0.030 |
2.00~2.50 |
0.90~1.10 |
SFVA F22B |
|||||||
SFVA F |
0.15 |
0.50 |
0.30~0.60 |
≤0.030 |
≤0.030 |
2.65~3.35 |
0.80~1.00 |
SFVA F21B |
|||||||
SFVA F |
0.15 |
0.50 |
0.30~0.60 |
≤0.030 |
≤0.030 |
4.00~6.00 |
0.45~0.65 |
SFVA F5B |
|||||||
SFVA F |
0.25 |
0.50 |
0.30~0.60 |
≤0.030 |
≤0.030 |
4.00~6.00 |
0.45~0.65 |
SFVA F5D |
|||||||
SFVA F9 |
0.15 |
0.50~1.00 |
0.30~0.60 |
≤0.030 |
≤0.030 |
8.00~10.0 |
0.90~1.10 |