收藏词条 编辑词条 热轧环件(YB/T4068-1991)
表1 热轧环件的尺寸规格 (mm)
外 径 | 高 度 | 内 径 | 壁 厚 |
600-2000 | 70-220 | ≥500 | 50-160 |
(2)牌号和化学成分见表2
表2 热轧环件的牌号和化学成分
牌号 | 化学成分(质量分数)(%) | ||||||
C | Si | Mn | Cr | M0 | P | S | |
10 | 0.07~ 0.14 | 0.17~ 0.37 | 0.35~ 0.65 |
|
| ≤0.035 | ≤0.035 |
15 | 0.12~ 0.19 | 0.17~ 0.37 | 0.35~ 0.65 |
|
| ≤0.035 | ≤0.035 |
20 | 0.17~ 0.24 | 0.17~ 0.37 | 0.35~ 0.65 |
|
| ≤0.035 | ≤0.035 |
25 | 0.22~ 0.30 | 0.17~ 0.37 | 0.50~ 0.80 |
|
| ≤0.035 | ≤0.035 |
30 | 0.27~ 0.35 | 0.17~ 0.37 | 0.50~ 0.80 |
|
| ≤0.035 | ≤0.035 |
35 | 0.32~ 0.40 | 0.17~ 0.37 | 0.50~ 0.80 |
|
| ≤0.035 | ≤0.035 |
40 | 0.37~ 0.45 | 0.17~ 0.37 | 0.50~ 0.80 |
|
| ≤0.035 | ≤0.035 |
45 | 0.42~ 0.50 | 0.17~ 0.37 | 0.50~ 0.80 |
|
| ≤0.035 | ≤0.035 |
50 | 0.47~ 0.55 | 0.17~ 0.37 | 0.50~ 0.80 |
|
| ≤0.035 | ≤0.035 |
16Mn | 0.12~ 0.20 | 0.20~ 0.55 | 1.20~ 1.60 |
|
| ≤0.035 | ≤0.035 |
50Mn | 0.48~ 0.56 | 0.17~ 0.37 | 0.70~ 1.00 |
|
| ≤0.035 | ≤0.035 |
40Cr | 0.37~ 0.44 | 0.17~ 0.37 | 0.50~ 0.80 | 0.80~ 1.10 |
| ≤0.030 | ≤0.030 |
42CrM0 | 0.38~ 0.45 | 0.17~ 0.37 | 0.50~ 0.80 | 0.90~ 1.20 | 0.15~ 0.25 | ≤0.030 | ≤0.030 |
42CrM0A | 0.38~ 0.45 | 0.17~ 0.37 | 0.50~ 0.80 | 0.90~ 1.20 | 0.15~ 0.25 | ≤0.025 | ≤0.025 |
50SiMn | 0.45~ 0.56 | 0.80~ 1.10 | 0.80~ 1.10 |
|
| ≤0.030 | ≤0.030 |
35SiMn | 0.32~ 0.40 | 1.10~ 1.40 | 1.10~ 1.40 |
|
| ≤0.030 | ≤0.030 |
35CrM0 | 0.32~ 0.40 | 0.17~ 0.37 | 0.40~ 0.70 | 0.80~ 1.10 | 0.15~ 0.25 | ≤0.030 | ≤0.030 |
50CrM0A | 0.45~ 0.54 | 0.17~ 0.37 | 0.50~ 0.80 | 0.90~ 1.20 | 0.15~ 0.25 | ≤0.025 | ≤0.025 |
注:钢中残余Cr、Ni、Cu含量应符合GB/T1591、GB/T699、GB/T3077相应标准规定。
(3)力学性能见表3表4。
表3 优质碳素钢结构钢环件的力学性能。
牌号 | 交货状态 | 壁厚/mm | 抗拉强度ób/MPa | 伸长率δ5(%) | 断面收缩率ψ(%) | 冲击吸收功Aku/J | 布氏硬度HBS10/3000 |
≥ | |||||||
15 | 正火 | ≤100 | 345 | 27 | 53 |
|
|
>100 | 335 | 25 | 50 |
| |||
20 | ≤100 | 390 | 24 | 53 |
|
| |
>100 | 370 | 23 | 50 |
| |||
25 | ≤100 | 420 | 22 | 48 | 39 |
| |
>100 | 390 | 20 | 46 | 31 | |||
30 | ≤100 | 470 | 19 | 45 | 31 |
| |
>100 | 460 | 18 | 40 | 24 | |||
35 | ≤100 | 510 | 18 | 43 | 31 |
| |
>100 | 490 | 18 | 40 | 24 | |||
40 | ≤100 | 550 | 17 | 40 | 24 |
| |
>100 | 530 | 17 | 36 | 24 | |||
45 | ≤100 | 590 | 15 | 32 | 31 | ≤241 | |
>100 | 570 | 15 | 30 | 27 | |||
50 | ≤100 | 610 | 13 | 30 | 31 | ||
>100 | 590 | 12 | 28 | 27 | |||
50Mn | ≤100 | 635 | 13 | 35 | 31 | 207-262 | |
>100 | 610 | 12 | 33 | 27 |
表4 合金结构钢环件的力学性能
牌号 | 交货状态 | 壁厚/mm | 抗拉强度ób/MPa | 伸长率δ5(%) | 断面收缩率ψ(%) | 冲击吸收功Aku/J | 布氏硬度HBS10/3000 |
≥ | |||||||
40Cr | 调质 | ≤60 | 785 | 9 | 35 | 31 | 207-206 |
61-80 | 735 | 9 | 30 | 27 | |||
81-140 | 685 | 9 | 30 | 24 | |||
35CrM0 | 调质 | ≤70 | 735 | 15 | 40 | 47 | 207-262 |
71-140 | 685 | 15 | 40 | 39 | |||
42CrM0(42CrM0A) | 调质 | ≤70 | 785 | 12 | 40 | 47 | 207-262 |
71-140 | 735 | 10 | 35 | 39 | |||
35SiMn | 调质 | ≤60 | 785 | 12 | 40 | 39 | 207-262 |
61-80 | 735 | 12 | 35 | 35 | |||
81-140 | 685 | 12 | 35 | 31 | |||
50SiMn | 调质 | ≤60 | 835 | 10 | 35 | 31 | 207-262 |
61-80 | 785 | 10 | 35 | 27 | |||
81-140 | 735 | 10 | 35 | 24 | |||
50CrM0A | 调质 | ≤140 | 835 | 8 |
| 39 | 255-31 |
表5 法兰环件的力学性能
牌号 | 交货状态 | 壁厚 /mm | 抗拉强度ób /MPa | 伸长率 δ5 (%) | 断面收缩率 ψ (%) | 冲击吸收功 Aku /J | 布氏硬度 HBS 10/3000 |
≥ | |||||||
10 | 正火 | ≤100 | 335 | 205 | 31 |
|
|
>100 | 315 | 185 | 30 |
| |||
15 | ≤100 | 355 | 205 | 27 |
|
| |
>100 | 335 | 185 | 26 |
| |||
20 | ≤100 | 370 | 215 | 24 | 43 | 109-156 | |
>100 | 370 | 195 | 23 | 39 | |||
25 | ≤100 | 420 | 235 | 22 | 39 | 111-170 | |
>100 | 390 | 215 | 20 | 39 | |||
16Mn | 正火或调质 | ≤100 | 490-610 | 295 | 20 | 47 | 120-180 |
>100 | 470-620 | 275 | 19 | 47 |
(4)用途:适用于制造齿圈、轴承圈、磨环及压力容器平焊法兰、高颈法兰、浮头钩圈法兰和高颈搪瓷法兰等。
(1)尺寸规格见表1。