收藏词条 编辑词条 合金结构钢(GB 3077-88)(二)
熔炼分析的化学成分③
钢组号 |
钢组 |
序 号 |
牌号 |
化 学 成 分 (%) |
|||||||||||
C (碳) |
Si (硅) |
Mn (锰) |
Mo (钼) |
W (钨) |
Cr (铬) |
Ni (镍) |
V (钒) |
Ti (钛) |
B (硼) |
Al (铝) |
Xt(加入量) |
||||
11 |
SiMnVB |
27 |
20SiMnVB |
0.17-0.24 |
0.50-0.80 |
1.30-1.60 |
― |
― |
― |
― |
0.07-0.12 |
― |
0.0005-0.0035 |
― |
― |
12 |
Cr |
28 |
15Cr |
0.12-0.18 |
0.17-0.37 |
0.40-0.70 |
― |
― |
0.70-1.00 |
― |
― |
― |
― |
― |
― |
29 |
15CrA |
0.12-0.17 |
0.40-0.70 |
||||||||||||
30 |
20Cr |
0.12-0.24 |
0.37-0.50 |
||||||||||||
31 |
30Cr |
0.27-0.34 |
0.80-1.10 |
||||||||||||
32 |
35Cr |
0.32-0.39 |
|||||||||||||
33 |
40Cr |
0.37-0.44 |
|||||||||||||
34 |
45Cr |
0.42-0.49 |
|||||||||||||
35 |
50Cr |
0.42-0.54 |
0.17-0.37 |
0.50-0.80 |
― |
― |
0.80-1.10 |
― |
― |
― |
― |
― |
― |
||
13 |
CiSi |
36 |
38CiSi |
0.35-0.43 |
1.00-1.30 |
0.30-0.60 |
― |
― |
1.30-1.60 |
― |
― |
― |
― |
― |
― |
14 |
C Mo |
37 |
12CrMo |
0.08-0.15 |
0.17-0.37 |
0.40-0.70 |
0.40-0.55 |
― |
0.40-0.70 |
― |
― |
― |
― |
― |
― |
38 |
15CrAMo |
0.12-0.18 |
0.80-1.10 |
||||||||||||
39 |
20CrMo |
0.17-0.24 |
0.15-0.25 |
||||||||||||
40 |
30CrMo |
0.26-0.34 |
|||||||||||||
41 |
30CrMoA |
0.26-0.33 |
|||||||||||||
42 |
35CrMo |
0.32-0.40 |
|||||||||||||
43 |
42CrMo |
0.38-0.45 |
0.50-0.80 |
0.90-1.20 |
钢组号 |
钢组 |
序 号 |
牌号 |
化 学 成 分 (%) |
|||||||||||
C (碳) |
Si (硅) |
Mn (锰) |
Mo (钼) |
W (钨) |
Cr (铬) |
Ni (镍) |
V (钡) |
Ti (钛) |
B (硼) |
Al (铝) |
Xt(加入量) |
||||
15 |
CrMoV |
44 |
12CrMoV |
0.008-0.15 |
0.17-0.37 |
0.40-0.70 |
0.25-0.35 |
― |
0.30-0.60 |
― |
0.15-0.30 |
― |
― |
― |
― |
45 |
35CrMoV |
0.30-0.38 |
0.20-0.30 |
1.00-1.30 |
0.10-0.20 |
||||||||||
46 |
12Cr1MoV |
0.08-0.15 |
0.25-0.35 |
0.90-1.20 |
0.30-0.50 |
||||||||||
47 |
25Cr2MoVA |
0.22-0.29 |
0.17-0.37 |
0.40-0.70 |
0.25-0.35 |
― |
1.50b-1.80 |
0.15-0.30 |
― |
― |
― |
― |
|||
48 |
25Cr2Mo1VA |
0.22-0.29 |
0.50-0.80 |
0.90-1.10 |
2.10b-2.50 |
0.30-0.50 |
|||||||||
16 |
CrMoWV |
49 |
20Cr2MoWVA |
0.17-0.24 |
0.17-0.37 |
0.30-0.60 |
0.35-0.50 |
0.30-0.60 |
2.60-3.00 |
― |
0.70-0.90 |
― |
― |
― |
― |
17 |
CrMoAI |
50 |
38CrMoAL |
0.35-0.42 |
0.20-0.45 |
0.30-0.60 |
0.15-0.25 |
― |
1.35-1.65 |
― |
― |
― |
― |
0.70-1.10 |
― |
18 |
CrV |
51 |
20CrV |
0.17-0.23 |
0.17-0.37 |
0.50-0.80 |
― |
― |
0.80-1.10 |
― |
0.10-0.20 |
― |
― |
― |
― |
52 |
40CrV |
0.37-0.44 |
|||||||||||||
53 |
50CrVA |
0.47-0.54 |
|||||||||||||
19 |
CrMo |
54 |
15CrMn |
0.12-0.18 |
0.17-0.37 |
1.10-1.40 |
― |
― |
0.40-0.70 |
― |
― |
― |
― |
― |
― |
55 |
20CrMn |
0.17-0.23 |
0.90-1.20 |
0.90-1.20 |
|||||||||||
56 |
40CrMn |
0.37-0.45 |
0.90-1.20 |
― |
― |
0.90-1.20 |
|||||||||
20 |
CrMoSi |
57 |
20CrMnSi |
0.17-0.23 |
0.90-0.29 |
0.80-1.10 |
― |
― |
0.80-1.10 |
― ― |
― ― |
― ― |
― ― |
― ― |
― ― |
58 |
25CrMnSi |
0.22-0.29 |
|||||||||||||
59 |
30CrMnSi |
0.27-0.34 |
0.90-1.20 |
1.80-1.10 |
0.80-1.10 |
||||||||||
60 |
30CrMnSiA |
0.28-0.34 |
|||||||||||||
61 |
35CrMnSiA |
0.32-0.39 |
1.10-1.40 |
|
1.10-1.40 |