收藏词条 编辑词条 电渣熔铸合金工具钢模块（YB/T155-1999）
(1)尺寸规格和允许偏差见表1、表2。
表1 电渣熔铸模块的截面尺寸系列(mm)
|
高度 H |
宽度B |
|||||||||||||||
|
250 |
300 |
350 |
400 |
450 |
500 |
550 |
600 |
650 |
700 |
750 |
800 |
850 |
900 |
950 |
1000 |
|
|
250 |
× |
× |
× |
× |
× |
|
|
|
|
|
|
|
|
|
|
|
|
275 |
|
× |
× |
× |
× |
× |
|
|
|
|
|
|
|
|
|
|
|
300 |
|
× |
× |
× |
× |
× |
× |
|
|
|
|
|
|
|
|
|
|
325 |
|
× |
× |
× |
× |
× |
× |
|
|
|
|
|
|
|
|
|
|
350 |
|
|
× |
× |
× |
× |
× |
× |
× |
|
|
|
|
|
|
|
|
375 |
|
|
|
|
× |
× |
× |
× |
× |
|
|
|
|
|
|
|
|
400 |
|
|
|
|
× |
× |
× |
× |
× |
× |
|
|
|
|
|
|
|
425 |
|
|
|
|
|
|
|
|
X |
× |
× |
× |
× |
|
× |
|
|
450 |
|
|
|
|
|
|
|
|
× |
× |
× |
× |
|
|
|
|
|
475 |
|
|
|
|
|
|
|
|
|
× |
|
× |
|
× |
|
× |
|
项目 尺寸 |
长度 L |
宽度 B |
高度 H |
|
<600 |
+4% O |
+4% O |
+4% O |
|
≥600 |
3% 0 |
3% 0 |
注：特殊尺寸的允许偏差由供需双方协商并在合同中注明或提供图样。
(2)牌号和化学成分见表3。
表3电渣熔铸模块的牌号和化学成分
|
牌 号 |
化学成分(质量分数)(%) |
||||||||
|
C |
Mn |
Sj |
Cr |
Ni |
M0 |
V |
P |
S |
|
|
5CrNiM0 |
0.50～0.60 |
0.50～0.80 |
≤0.40 |
0.50～0.80 |
1.40～1.80 |
0.15～0.30 |
|
≤0.030 |
≤0.030 |
|
5CrMnMo |
0.50～0.60 |
1.20～1.60 |
0.25～0.60 |
0.60～0.90 |
|
0.15～0.30 |
≤0.030 |
≤0.030 |
|
|
4CrMIlSiMOV |
0.35～0.45 |
0.80～1.10 |
0.80～1.10 |
1.30～1.50 |
|
0.40～0.60 |
0.20～0.40 |
≤0.030 |
≤0.030 |
|
4SiMnMoV |
0.40～0.50 |
0.80～1.10 |
0.80～1.10 |
|
0.40～0.60 |
0.20～0.40 |
≤0.030 |
≤0.030 |
|
注：残余cu质量分数不大于0.30%；Ni不作合金元素时，残余M质量分数不大于0.25%。
(3)力学性能
1)模块经退火、机械粗加工后交货。
2)交货状态的模块的布氏硬度为197-241HBS。
(4)用途适用于制造模锻锤和机械锻压机用的模块。各牌号推荐使用范围：
1)5CrNiMo钢适用于3-10t锤以下的浅槽型(<30mm)模块。
2)5CrMnMo钢适用于3t锤以下的浅槽型(<30mm)模块。
3)4SiMnMoV钢适用于高度尺寸小于375mm型槽复杂的模块。
注：l模块长度由需方在合同中注明或提供图样。
2其他特殊截面尺寸由供需双方协商并提供图样。
表2 电渣熔铸模块的长、宽、高尺寸允许偏差(mm)